Improving Hydrophobicity and Water Vapor Barrier Properties in Paper Using Cellulose Nanofiber-Stabilized Cocoa Butter and PLA Emulsions

This study explores the use of cellulose nanofiber (CNF)-stabilized Pickering emulsions for paper coatings, focusing on their rheological properties and effects on hydrophilicity and water vapor transmission rate (WVTR). Two types of Pickering emulsions, oil-in-water (O/W), were stabilized with 1 wt% CNF extracted from fique by-products. The oily phases of the emulsions were composed of poly(lactic acid) (PLA) and cocoa butter (CB). The physical stability, viscosity, and viscoelasticity of the emulsions were characterized. The emulsions were applied to the surfaces of Bond and Kraft papers using the rod-coating method. The coating process involved first applying a layer of the PLA emulsion followed by a layer of the CB emulsion. The coated papers were then evaluated by FE-SEM, contact angle, adhesion work, and water vapor transmission rate (WVTR). The results indicated that the coatings effectively produced a slightly hydrophobic surface on the papers, with contact angles approaching 90°. Initially, Kraft paper exhibited a WVTR value of 29.20 ± 1.13 g/m²·h, which significantly decreased to 7.06 ± 2.80 g/m²·h after coating, representing a reduction of 75.82%. Similarly, natural Bond paper showed a WVTR value of 30.56 ± 0.34 g/m²·h, which decreased to 14.37 ± 5.91 g/m²·h after coating, indicating a reduction of 47.02%. These findings demonstrate the potential of CNF-stabilized Pickering emulsions for enhancing the performance of paper coatings in terms of hydrophobicity and moisture barrier properties. The approach of this study aligns with global sustainability goals in packaging materials combining the use of PLA and CB to develop a waterborne coating to enhance the moisture barrier properties, demonstrated by a substantial reduction in water vapor transmission rates, and an improved hydrophobicity of coated papers.