Activated Carbon Bio-xerogels as Electrodes for Super Capacitors Applications

Zulamita Zapata-Benabithe, Giovanna Diossa, Chris D. Castro, Germán Quintana

Resultado de la investigación: Contribución a una revistaArtículo de la conferenciarevisión exhaustiva

20 Citas (Scopus)

Resumen

The objectives of this work are to evaluate the use of the lignin as precursor of carbon xerogels and to determinate the effect of porosity and surface functionalities on the electrochemical capacitance of the activated carbon bio-xerogels. Lignin replaced the resorcinol at a mass fraction between 0 and 0.086 (wt%). The organic carbon xerogels are H3PO4-activated at H3PO4/carbon ratio of 1/1 at 450°C to increase pore volume and surface area. Gravimetric capacitance values at 0.125 A/g, in a three-cell configuration, ranged from 138 to 234 F/g. Sample with a 0.086 content of lignin showed the best electrochemical behavior, which was associated with the high BET surface area (1243 m2/g), high volume (W0(N2)= 0.518 cm3/g) and width micropores (L0(N2)= 1.43 nm) and to the presence of pseudo faradic effects.

Idioma originalInglés
Páginas (desde-hasta)18-24
Número de páginas7
PublicaciónProcedia Engineering
Volumen148
DOI
EstadoPublicada - 2016
Publicado de forma externa
Evento4th International Conference on Process Engineering and Advanced Materials, ICPEAM 2016 - Kuala Lumpur, Malasia
Duración: 15 ago. 201617 ago. 2016

Nota bibliográfica

Publisher Copyright:
© 2016 The Authors. Published by Elsevier Ltd.

Huella

Profundice en los temas de investigación de 'Activated Carbon Bio-xerogels as Electrodes for Super Capacitors Applications'. En conjunto forman una huella única.

Citar esto