Concretes of low environmental impact obtained by geopolymerization of Metakaolin

This work shows results of partial replacement of Portland Type I cement®, by geopolymers obtained through alkaline activation of Metakaolin, in concrete mixtures. Replacement was made with 10%, 20% and 30% of geopolymers at 7, 14, 28 and 90 days of setting. Cement samples was mechanical and electrically tested. Mechanical resistance to compression assay shows that the best percentage of replacement is 10% for every setting time; highest value is 26.75MPa at 90 days. Nyquist diagrams at different times of immersion exhibit same trend: decreasing of electrical resistance as time of assay goes by.