Effect of degree of refining on flexural response of fibre cement boards reinforced with Guadua Angustifolia Kunth Bamboo

Luz Adriana Sánchez Echeverri, Jorge Alberto Medina Perilla, Germán Quintana, Jorge Hernán Sánchez Toro, Eshmaiel Ganjian

Resultado de la investigación: Contribución a una revistaArtículo de la conferenciarevisión exhaustiva

Resumen

In this research, alkaline pre-treated Guadua Angustifolia fibres were refined in a PFI mill refiner at different speeds (1500, 4500, 7000 and 10000 rev) and used as reinforcement in cement composite boards CCB. To determine physical changes after refining, Water Retention Value (WRV), Fibre length and SEM images were evaluated. Additionally, crystalline indices were calculated by Segal method from XRD spectra. With the aim to evaluate the effect of degree of refining in the mechanical response of CCB its flexural strength was evaluated after 7 and 28 days of curing. Results show an increasing of WRV up to 4500 rev of refining, followed by a decrease once this point of refining is overcome. Likewise, flexural strength of composites shows a similar behaviour as WRV, exhibiting an optimal value between 4500 and 7000 rev of refining.

Idioma originalInglés
PublicaciónSustainable Construction Materials and Technologies
Volumen2
EstadoPublicada - 2019
Publicado de forma externa
Evento5th International Conference on Sustainable Construction Materials and Technologies, SCMT 2019 - Kingston upon Thames, Reino Unido
Duración: 14 jul. 201917 jul. 2019

Nota bibliográfica

Publisher Copyright:
© 2019 International Committee of the SCMT conferences. All rights reserved.

Huella

Profundice en los temas de investigación de 'Effect of degree of refining on flexural response of fibre cement boards reinforced with Guadua Angustifolia Kunth Bamboo'. En conjunto forman una huella única.

Citar esto