Intermetallic-Rich Layer Formation for Improving Corrosion Resistance of Magnesium Alloys

D. Calderón, Y. Galindez, L. Toro, A. A. Zuleta, A. Valencia-Escobar, P. Chacón, E. Correa, F. Echeverría

    Producción científica: Contribución a una revistaArtículo en revista científica indexadarevisión exhaustiva

    7 Citas (Scopus)

    Resumen

    Abstract: The present work examines the formation of a corrosion protective coating containing intermetallic phases on magnesium alloy substrates. The protective coating was formed on the surfaces of commercially pure magnesium (cp Mg) and AZ31B magnesium alloy by vacuum thermal evaporation of commercially pure aluminium (cp Al) and a subsequent heat treatment of the sample. This coating was continuous, homogenous and its microstructure was a eutectic phase composed by clusters of α-Mg surrounded by β phase (Mg17Al12). This eutectic-type coating provided 168 and 504 h of protection inside the salt spray chamber for the cp Mg and AZ31 alloy samples, respectively. To achieve this, it was required to deposit at least 5.5 µm of cp Al and then perform a combined thermal treatment involving heating the samples to 583 K for 60 min and then raising the temperature to 693 K for 5 min. Graphic Abstract: [Figure not available: see fulltext.]

    Idioma originalInglés
    Páginas (desde-hasta)657-665
    Número de páginas9
    PublicaciónMetals and Materials International
    Volumen28
    N.º3
    DOI
    EstadoPublicada - mar. 2022

    Nota bibliográfica

    Publisher Copyright:
    © 2021, The Korean Institute of Metals and Materials.

    Tipos de Productos Minciencias

    • Artículos de investigación con calidad A1 / Q1

    Huella

    Profundice en los temas de investigación de 'Intermetallic-Rich Layer Formation for Improving Corrosion Resistance of Magnesium Alloys'. En conjunto forman una huella única.

    Citar esto