Tribological behavior of electroless Ni-B coatings on magnesium and AZ91D alloy

E. Correa, A. A. Zuleta, L. Guerra, M. A. Gómez, J. G. Castaño, F. Echeverría, H. Liu, P. Skeldon, G. E. Thompson

Resultado de la investigación: Contribución a una revistaArtículorevisión exhaustiva

56 Citas (Scopus)

Resumen

Ni-B coatings have been deposited directly on commercial purity magnesium and AZ91D alloy and characterized using glow discharge optical emission spectroscopy, scanning electron microscopy, X-ray diffraction and, for tribological and mechanical evaluation, dry sliding wear and friction testing and microhardness measurement. The boron content of the coating on Mg was slightly lower than that of the coating on the AZ91D alloy. The wear rates were similar for both coatings and two magnitude orders lower than those of the substrates. The coefficients of friction were similar for both coatings, in the range ~0.31 to 0.34. The values were close to that of the uncoated magnesium, while that for the AZ91D alloy was slightly lower, namely ~0.25. The wear mechanism of the electroless Ni-B coatings was governed by the presence of abrasive wear, delamination and tribo-corrosion processes.

Idioma originalInglés
Páginas (desde-hasta)115-123
Número de páginas9
PublicaciónWear
Volumen305
N.º1-2
DOI
EstadoPublicada - 30 jul. 2013
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'Tribological behavior of electroless Ni-B coatings on magnesium and AZ91D alloy'. En conjunto forman una huella única.

Citar esto